SMT Defect List and SMT Troubleshooting (SMT / SMD Problem and Solution)

SMT (Surface Mount Technology), like other SMD Soldering and PCB assembly technology is not ZERO-Defect soldering process. There will always be some or the other defect in any Electronics PCB assembly in both Thru-Hole and SMT.

Here I will discuss some of the most common faults and causes of SMT defects and possible solution and troubleshooting.

Common Faults in SMT:

  • Solder balls
  • Solder beading
  • Bridging
  • Open- Insufficient
  • Tombstoning
  • Unmelted paste
  • Excessive filet
  • Slump
  • Dewetting
  • Disturb joint
  • Orange Skinning

Solder BallsPossible cause:

  1. Solder Paste smearing on underside of stencil.
  2. What is squeegee pressure?
  3. Is stencil underside cleaned with a solvent and is solvent still present after cleaning?
  4. Is stencil proper aligned with PCB?

Solution to Solder Ball Problems:

  1. Check squeegee pressure
    Solder balls = numerous tiny solder balls trapped along the outside edge of the flux residue

    Solder balls = numerous tiny solder balls trapped along the outside edge of the flux residue

  2. Check for proper gasketting and alignment
  3. Check if cleaning solvent is completely evaporated before printing

Oxidised paste – Possible cause

  1. Was paste shipped refrigerated?
  2. Did paste spend a long time in a hot area?
  3. Was old paste returned to jar?
    Solder balls = numerous tiny solder balls trapped along the outside edge of the flux residue

    Solder balls = numerous tiny solder balls trapped along the outside edge of the flux residue

  4. Was jar put back into refrigeration after opening?
  5. Is alloy sensitive to oxidation?

Solution to Oxidised Solder Paste Problems:

  1. Run fresh paste from a different lot under same conditions and see if solder bars go away.

Oxidised paste – Possible cause

  1. Squeegee pressure too high
  2. Paste gets squeezed out between stencil and board

Solution: Reduce squeegee pressure

Possible cause:

  1. Drying out of paste after printing
  2. What is specified tack time of paste?

Solution: Run a PCB with fresh paste and see if problem goes away

Possible cause:

  1. Too slow ramp up in reflow profile

Solution: Run recommended profile and see if problem stays

Possible cause:

  1. Too rapid ramp up in flow profile

Solution: Run a slower ramp up profile to give volatiles to evaporate

SOLDER BEADS – Possible cause:

  1. Reflow profile ramp up slow
    Solder beading : solder balls that are alongside a components

    Solder beading : solder balls that are alongside a components

  2. Capillary action draws unreflowed paste away from pad to somewhere under the component, it reflows there and form a bead of solder which comes out from under the component side.

Solution: Run a more rapid ramp up profile of 1.5 Degree Celsius to 2.5 Degree Celsius per second.

Possible cause:

  1. Excessive amount of solder paste on component pads
  2. What is stencil thickness?
  3. Are apertures reduced?
  4. Dispense time for a dot?

Solution:

  1. Reduce aperture size of stencil or use thinner stencil
  2. Use smaller needle and/or reduce purge time on dispenser

Possible cause: Paste smearing on underside of stencil

  1. What is squeegee pressure?
  2. Is stencil underside cleaned with a solvent and is solvent still present after cleaning?
  3. Is stencil properly aligned with PCB?

Solution:

  1. Check squeegee pressure
  2. Check for proper gasketting and alignment
  3. Check if cleaning solvent is completely evaporated before printing

BRIDGING – Possible Cause:

  1. Cold slumping
    Bridging = solder running from one component contact to another resulting in a short circuit

    Bridging = solder running from one component contact to another resulting in a short circuit

  2. Is paste flowing apart after printing, height of deposit reduces and surface increases.

Solution:

  1. Check viscosity of paste, too low viscosity may result in cold slumping
  2. Check print speed, too rapid print speed may result in shearing of paste and degrading its thickness
  3. Check temperature in printer, too high temperature brings viscosity down
    Bridging = solder running from one component contact to another resulting in a short circuit

    Bridging = solder running from one component contact to another resulting in a short circuit

Possible Cause:

  1. Hot slumping
  2. Is paste flowing apart during ramp up part of reflow profile

Solution: Shorten duration of ramp up cycle in reflow profile

Possible Cause:

  1. Paste smearing on underside of stencil
  2. Paste can be outside pad area and form solder balls between two component leads resulting in a bridge

Solution – Reduce squeegee and check pcb-stencil alignment and gasketting

Possible Cause:

  1. Excessive solder paste being deposited on the pads
  2. While placing a component on the pads the paste is smeared out and may form a bridge to an adjacent pad

Remedy:

  1. Reduce amount of solder paste
  2. Increasing print speed may
  3. Reduce stencil thickness

Open-insufficientPossible cause:

Opens and insufficient = insufficient or no solder to make a complete bond between the lead and the pad

Opens and insufficient = insufficient or no solder to make a complete bond between the lead and the pad

  1. Scooping during printing
  2. Excessive squeegee pressure on a polypropylene squeegee may cause scooping

Remedy: Reduce squeegee pressure or use a harder durometer type of squeegee or use a metal squeegee

Possible Cause: Blocking of stencil aperture with dried up paste

Remedy: Unblock apertures and clean stencil

Possible Cause:

Opens and insufficient = insufficient or no solder to make a complete bond between the lead and the pad

Opens and insufficient = insufficient or no solder to make a complete bond between the lead and the pad

  1. Foreign material on solder pad
  2. Was solder mask printed on pad?

Remedy: Use another PCB

Possible Cause:

  1. Too high squeegee speed
  2. Paste cannot get into the apertures

Remedy: Reduce squeegee speed

Possible cause: Solder paste viscosity and/or metal content too low

Remedy: Check viscosity and metal content

TOMBSTONING

Tombstoning = chip type components standing up on one end after reflow caused by unequal forces on the components end

Tombstoning = chip type components standing up on one end after reflow caused by unequal forces on the components end

Possible cause: Unequal placement of components on pads prior to Reflow results in unbalanced solder forces.

Remedy: Check if placement equipment places properly.

Possible cause: Unequal heat sink i.e. ground planes inside PCB layers may draw heat away from pad.

Remedy: Increase soak time (plateau) or reflow profile so that all components are on.

UNMELTED PASTEPossible cause:

  1. To cold reflow profile
  2. Solder paste cannot melt completely
Unmelted paste = paste shows characteristics of powder after reflow, joints are dull not shiny. May be on some components only

Unmelted paste = paste shows characteristics of powder after reflow, joints are dull not shiny. May be on some components only

Remedy: Check reflow profile, make sure peak temperature and time above liquids (183C) are high enough and soak (plateau) is long enough.

Unmelted paste = paste shows characteristics of powder after reflow, joints are dull not shiny. May be on some components only

Unmelted paste = paste shows characteristics of powder after reflow, joints are dull not shiny. May be on some components only

Excessive Fillet

Possible cause: Too much solder paste deposited on pads

Remedy:

  1. If excess solder occurs on all components reduce overall stencil thickness or reduce dispenser purge time
  2. If excess solder occurs on some places only reduce stencil thickness or dispense purge time for these components only
Excessive fillet = bulbous appearance of joint where outlines of the leads are obscured by the quantity of solder on them

Excessive fillet = bulbous appearance of joint where outlines of the leads are obscured by the quantity of solder on them

Slump Cold SlumpPossible cause:

Viscosity of paste to low or metal content to low

Slump = deformation of paste deposit after printing or dispensing deposit height will reduce while surface expands

Slump = deformation of paste deposit after printing or dispensing deposit height will reduce while surface expands

Remedy: Use different type of paste with higher viscosity or higher metal content

Possible cause: Paste came in contact with a cleaning solvent or other alien product

Remedy:

  1. Make sure there are no solvents presents after cleaning the screen
  2. Never try to revive the paste by adding some compound

Possible cause:

Slump = deformation of paste deposit after printing or dispensing deposit height will reduce while surface expands

Slump = deformation of paste deposit after printing or dispensing deposit height will reduce while surface expands

  1. Squeegee pressure to high
  2. Paste is shearing due to excessive pressure applied to it thickeners in paste are destroyed

Remedy: Use new paste and reduce squeegee pressure

Possible cause: Temperature of paste is too high while printing or dispensing

Remedy:

  1. Check temperature inside printer
  2. Reduce pressure on squeegee
  3. Reduce on pressure on syringe when dispensing

Hot Slump

Possible cause: Too slow ramp up in reflow profile

Remedy: Increase ramp up temperature, make sure to have a ramp up between 2 Degree Celsius to 3 Degree Celsius per second

DEWETTINGPossible cause:

Dewetting = bad attachment of molten solder to surface

Dewetting = bad attachment of molten solder to surface

  1. Unwanted material on surface which prevents solder from attaching to surface, i.e. solder mask, fingerprints or oxides.

Remedy:

  1. Clean boards first
  2. Use different batch of boards

Possible cause:

Dewetting = bad attachment of molten solder to surface

Dewetting = bad attachment of molten solder to surface

  1. Bad alloy in HAL process, i.e. too much Cu elevates melting point of HAL alloy

remedy:

  1. Increase peak temperature in reflow
  2. Use different batch of boards

Disturbed Joint Possible cause:

A source of vibration that is transmitted through the pcb during the liquids state of the reflow profile

Remedy:

  1. Find and fix source of vibration
  2. Adjust reflow
Disturbed Joint = dull, rough appearance of solder in an alloy that is normally bright and shiny

Disturbed Joint = dull, rough appearance of solder in an alloy that is normally bright and shiny

Orange skinningPossible cause:

Orange skinning = dull, rough appearance of solder, joint texture is orange skin like

Orange skinning = dull, rough appearance of solder, joint texture is orange skin like

  1. Too high in peak zone
  2. Residue is burned or rosin was cooking

Remedy:

  1. Lower peak zone temperature

Possible cause:

  1. Too long exposure to temperatures between activation temp and reflow = (depending on alloy)

Remedy:

Orange skinning = dull, rough appearance of solder, joint texture is orange skin like

Orange skinning = dull, rough appearance of solder, joint texture is orange skin like

  1. Shorten time in soak or lower soak temperatures

Possible cause:

  1. Preheating too high

Remedy:

  1. Lower preheat temperatures

Use Nowadays SMT Equipment can reduce the SMT Defect to a very low level:

Automatic SMT Production Line:

PCB LoaderSMT Stencil PrinterPCB ConveyorSPIPick and Place MachineAOISMT Reflow OvenAOIPCB UnloaderDIP Component Insert LineWave Soldering MachineTHT PCB unloader

Keywords:

SMT Assembly line, PCB Assembly line, LED Production line, Automatic SMT Assembly line,Semi Automatic SMT Assembly line, JUKI Assembly Line, Samsung Assembly Line, HanwhaAssembly Line, Panasonic Assembly Line, Siemens Assembly Line, FUJI Assembly Line,Yamaha Assembly Line.

我司提供 SMT设备整体解决方案, 包括 回流焊无铅回流焊无铅波峰焊贴片机锡膏印刷机上下板机接驳台AOI光学检测设备SMT生产线SMT配件  等设备, 如果有任何需要, 请联系我们:吴先生,微信:13691605420, Email: sales@flason-smt.com
1) 1)这是我第一次购买SMT设备,请问它容易操作吗?
我们会提供使用说明书和视频操作教程,像贴片机,回流焊等大机器可以上门安装,培训,费用由你们出,买方也可以安排工程师到我们公司免费培训,食宿费用需要你们出。如果还有问题可以联系我们的销售及售后解决。
2) 如果机器在使用过程中遇到问题,该如何处理 ?
详细描述问题,告诉我们,并配合我们查找具体原因。找到原因后,如果需要更换配件的,在保修期内免费更换,出了保修期,需要支付一定成本及快递费。珠三角区域我们又有工程师定期处理售后问题。其他区域也可以派工程师上门服务。
3) 最小订单量?
一台机器。
4) 该如何订购SMT设备?
联系我司销售人员,他会详细了解您的需要,提供解决方案,并生成订单,双方确认无误后即可安排货款及生产SMT设备.深圳或珠三角周边简易防水包装,其他省份木箱包装。
5)为什么选择我们?
A. 10年SMT设备生产经验 !
B. 阿里金品诚企 !
C. 最好的质量! 最好的单价 ! 最好的服务 !

联系我们

Contact: 吴先生

Phone: +86 13691605420

Tel: 0755-85225569

Email: sales@flason-smt.com

Add: 深圳宝安区松岗街道燕川社区广田路94号